前言：ABS马来西亚东丽1990X88,马来西亚东丽1990X88 ABS990X88,990X88原料供应
物性性能测试条件测试方法测试结果测试单位密度ASTM D792/ISO 11831.08吸水率 23℃/24HASTM D570/ISO 620.3%熔融指数（流动系数）ASTM D1238/ISO 113319~23g/10min机械性能测试条件测试方法测试结果测试单位拉伸强度ASTM D638/ISO 527490（屈服）380（断裂）kg/cm?(MPa)[Lb/in?]伸长率ASTM D638/ISO 5273.5%洛氏硬度ASTM D785R-115弯曲模量ASTM D790/ISO 17823500kg/cm?(MPa)[Lb/in?]弯曲强度ASTM D790/ISO 178780kg/cm?(MPa)[Lb/in?]屈服强度23℃kg/cmASTM D-638490洛氏硬度23℃RASTM D-785115屈服下的拉伸23℃%ASTM D-638断裂强度下的拉伸23℃%ASTM D-638挠曲极限23℃kg/cmASTM D-790冲击强度12.7×12.7×62.5mm(带韧口)，23℃；0℃；-30℃kg.cm/cmASTM D-256冲击强度3.2×12.7×62.5mm(带韧口)，23℃；0℃；-30℃kg.cm/cmASTM D-256挠曲强度23℃kg/cmASTM D-790780断裂强度23℃kg/cmASTM D-638380拉伸断裂伸长率(延伸率)ASTM D638/ISO 52730%IZOD 缺口冲击强度ASTM D256/ISO 17913kg·cm/cm(J/M)ft·lb/inIZOD 缺口冲击强度ASTM D256/ISO 1796kg·cm/cm(J/M)ft·lb/in热性能测试条件测试方法测试结果测试单位燃烧性（率）UL94HB热变形温度ASTM D648/ISO 7589℃（℉）线性膨胀系数ASTM D696/ISO 113591.2x10^-4mm/mm.℃燃烧性UL-94线性膨胀系数ASTM D-696热变形温度18.56kg/cm℃ASTM D-64889基本性能测试条件测试方法测试结果测试单位吸水性浸入23℃水中24小时%ASTM D-5700.3熔融指数220℃/10.0kgg/10minASTM D-1238其他性能测试条件测试方法测试结果测试单位熔融粘度220℃×10插入式粘度计