前言：台湾奇美HIPS,HIPSPH-879,台湾奇美PH-879,PH-879物性,PH-879塑胶原材料
物性表物性性能测试条件测试方法测试结果测试单位熔融指数（流动系数）ASTM D1238/ISO 113310.0g/10min机械性能测试条件测试方法测试结果测试单位洛氏硬度ASTM D78575弯曲模量ASTM D790/ISO 1781.7(2.4)kg/cm?(MPa)[Lb/in?]弯曲强度ASTM D790/ISO 178410(5820)kg/cm?(MPa)[Lb/in?]弯曲弹性率ASTM D-7901.7(2.4)洛式硬度ASTM D-78575L弯曲强度ASTM D-790410(5820)kg/cm延伸率ASTM D-63845%引张强度ASTM D-638300(4260)kg/cmIZOD 缺口冲击强度ASTM D256/ISO 1797.0(1.28)kg·cm/cm(J/M)ft·lb/inIZOD 缺口冲击强度ASTM D256/ISO 1798.5(1.56)kg·cm/cm(J/M)ft·lb/inIZOD冲击强度1/4"ASTM D-2567.0(1.28)kg.cm/cm(ft.lb/in)IZOD冲击强度1/8"ASTM D-2568.5(1.56)kg.cm/cm(ft.lb/in)热性能测试条件测试方法测试结果测试单位燃烧性（率）UL941/16"V0热变形温度ASTM D648/ISO 7580(176)℃（℉）维卡软化点ASTM D1525/ISO R30694(201)℃（℉）热变形温度ASTM D-64880(176)℃(°F)维卡软化点ASTM D-152594(201)℃(°F)燃烧率File No E56070 UL&C-CL1/16"V0基本性能测试条件测试方法测试结果测试单位熔融指数ASTM D-123810.0(Cond.G)g/10min