前言：香港盛禧奥斯泰隆438 ,438应用优势,高性能材料438,HIPS438 物性,HIPS斯泰隆438
物性表
| 模具收缩率 | ASTM D-955 | 0.40-0.70 | % |
| 拉伸屈服强度 | ASTM D-638 | 33.1 | Mpa | |
| 伸长率 | 断裂 | ASTM D-638 | 40 | % |
| 弯曲模量 | ASTM D-790 | 2560 | Mpa | |
| 弯曲强度 | ASTM D-790 | 58.6 | Mpa | |
| IZOD缺口冲击强度 | 23℃ | ASTM D-256 | 90.7 | J/m |
| 热变形温度 | 1.80MPa，未退火 | ASTM D-648 | 77.2 | °C |
| 热变形温度 | 1.80MPa，退火 | ASTM D-648 | 98.9 | °C |
| 维卡软化温度 | ASTM D-1525 | 105 | °C | |
| 线形热膨胀系数 | Flow | ASTM D-696 | 0.000076 | cm/cm/℃ |
| 阻燃性 | 1.50mm | UL 94 | HB |
| 熔融指数 | 200℃/5kg | ASTM D-1238 | 5.0 | g/10min |