前言：泰国科思创拜耳6555,PC塑料6555,6555聚碳酸酯塑料,PC阻燃级6555,pc注塑挤出型6555
物性表物理性能测试条件测试方法测试结果测试单位密度 / 比重23°CISO11831.20g/cm?表观密度2ISO600.64g/cm?熔体质量流动速率300°C/1.2kgISO113310g/10min熔体体积流动速率300°C/1.2kgISO113310.0cm3/10min收缩率TDISO25770.60to0.80%收缩率MDISO25770.60to0.80%收缩率TD:2.00mm3ISO294-40.75%收缩率MD:2.00mm3ISO294-40.70%吸水率饱和,23°CISO620.30%吸水率平衡,23°C,50%RHISO620.12%机械性能测试条件测试方法测试结果测试单位弯曲应力423°CISO17898.0Mpa弯曲应变523°CISO1787.1%拉伸模量23°CISO527-2/12400Mpa拉伸应力屈服,23°CISO527-2/5066.0Mpa拉伸应力断裂,23°CISO527-2/5070.0Mpa拉伸应变屈服,23°CISO527-2/506.2%拉伸应变断裂,23°CISO527-2/50130%标称拉伸断裂应变23°CISO527-2/50>50%TensileCreepModulus1hrISO899-12200Mpa拉伸蠕变模量1000hrISO899-11900Mpa弯曲模量423°CISO1782400Mpa弯曲应力43.5%Strain,23°CISO17874.0Mpa热性能测试条件测试方法测试结果测试单位热变形温度0.45MPa,未退火ISO75-2/B137°C热变形温度1.8MPa,未退火ISO75-2/A125°C玻璃转化温度8ISO11357-2145°C维卡软化温度--ISO306/B50144°C维卡软化温度--ISO306/B120145°CBallPressureTest136°CIEC60695-10-2Pass线形热膨胀系数MD：23到55°CISO11359-26.5E-05cm/cm/°C线形热膨胀系数TD：23to55°CISO11359-26.5E-05cm/cm/°C导热系数923°CISO83020.20W/m/KRTIElec1.5mmUL746125°CRTIImp1.5mmUL746115°CRTIStr1.5mmUL746125°C电气性能测试条件测试方法测试结果测试单位表面电阻率IEC600931E+16ohms体积电阻率23°CIEC600931E+16ohms·cm介电强度23°C,1.00mmIEC60243-134KV/mm相对电容率23°C,100HzIEC602503.10相对电容率23°C,1MHzIEC602503.00耗散因数23°C,100HzIEC602508E-04耗散因数23°C,1MHzIEC602509E-03漏电起痕指数解决方案AIEC60112225V漏电起痕指数解决方案BIEC60112125V