前言：FR370高性能材料,旭化成PA66供应商,日本FR370材料特性,FR370应用案例分析,PA66旭化成FR370
物性纠错 | 更多>>物性性能测试条件测试方法测试结果测试单位密度ASTM D792/ISO 11831.16成型收缩率ASTM D9550.9-1.6%吸水率 23℃/24HASTM D570/ISO 622.3%物理性能测试条件测试方法测试结果测试单位收缩率MD内部方法0.90to1.6%收缩率干旭化成方法0.9-1.6%磨耗率湿ASTM D-10447机械性能测试条件测试方法测试结果测试单位洛氏硬度干(湿)ASTM D-785120(110)R scale断裂延伸率干(湿)ASTM D-6387(70)%悬臂梁式缺口冲击强度干(湿)ASTM D-25629(58)J/m抗挠强度干(湿)ASTM D-790128(56)Mpa抗挠系数干(湿)ASTM D-7903.3(1.3)GPa洛氏硬度干(湿)ASTM D-78585(55)M Scale拉伸强度干(湿)ASTM D-63883(58)Mpa拉伸模量23°CISO527-23600Mpa抗张强度ASTMD63883.0Mpa拉伸应力屈服,23°CISO527-283.0Mpa拉伸应力断裂,23°CISO527-280.0Mpa拉伸应变屈服,23°CISO527-24.5%伸长率断裂ASTMD6387.0%拉伸应变断裂,23°CISO527-215%弯曲模量ASTMD7903300Mpa弯曲模量23°CISO1783600Mpa弯曲强度ASTMD790128Mpa弯曲应力23°CISO178124Mpa断裂伸长率ASTM D638/ISO 5277%