前言：PA66日本东丽,CM3004,PA66,PA66 CM3004,CM3004日本东丽
CM3004-V0
聚亚己基己二酸酰胺#聚己二酰己二胺|尼龙66|PA66
日本东丽
填充物:阻燃
物性信息：
| 吸水率 ((24小时)23°C) | 1.1 | % | ASTM D-570 |
| 抗燃级 | 113 | UL 94 | |
| 比重 | 1.18 | ASTM D-792 |
| 抗拉断裂强度 (23°C) | 12 | kg/cm | ASTM D-638 |
| 埃佐德卫声 (无缺口1/2" 23°C) | 5 | kg.cm/cm | |
| 抗拉屈股强度 (23°C) | 850 | kg/cm | ASTM D-638 |
| 挠曲强度 (-40°C) | 1210 | kg/cm | ASTM D-790 |
| 挠曲模量 (-40°C) | 34500 | kg/cm | ASTM D-790 |
| 抗电弧性 (1/8") | 127 | ASTM D-150 | |
| 介电强度 (1/8" 短时间) | 17 | KV/mm | ASTM D-149 |
| 体积电阻率 | V-0 | Ω.cm | ASTM D-257 |
| IEC导电径踪指数 (导热率温度指表) | 600<= | V | UL 746 |